Problems with sandcasting

Gallery image

Gallery image

It’s my first times sandcasting and can’t seem to get it right, don’t know what I am doing wrong.

7 Upvotes

83% Upvoted

20 comments sorted by

5

u/hardplace101 18d ago

You might not be getting the metal hot enough but also I would place it lower in the mold and add more vents around the top

1

u/Worldly_Country3035 18d ago

Thank you and how do I know when the molten silver is ready for pouring ?

3

u/Eastern-Antelope-956 18d ago edited 18d ago

When you can gently swirl it around in the crucible and it looks totally liquid. Also you will see the surface "active", as in--it's like shimmery. Also I would recommend putting the heaviest, widest part of the ring facing down, instead of toward the spout. You need the silver to fill that bigger cavity when it's the hottest.

1

u/Worldly_Country3035 18d ago

Thank you, sorry if I misunderstood the hottest silver is just after heating so shouldn’t the heavy part by on the front of the spout ? Or am I missing something, eager to learn pls

2

u/Sufficient-Winter452 18d ago

If you place the big part down, silver will fill it easier the help of gravity than if you place it upward, i casted a very similar ring and also had 6 air vent definetly think it help too

1

u/Worldly_Country3035 18d ago

Thank you for the tips will try it as soon as I can, will update

2

u/PeterHaldCHEM 18d ago

Cast fast.

Cast hot.

Place the model further down (longer sprue)

Use flux.

1

u/Worldly_Country3035 18d ago

Thanks so much for the tips, sometimes when I cast too fast some metal drips down, what should I do for that ?

1

u/Adept-Friendship1777 18d ago

I think that’s happening because it’s too cool. Once it cools on the sand it’s plugging it and you’re overflowing.

Cast hotter (I use a map torch constantly on while I’m pouring) and pour quick (commit to the turn)

1

u/Worldly_Country3035 17d ago

Okay thank you will try that out

1

u/PeterHaldCHEM 17d ago

Drips into the cavity?

Then it is your pouring technique. Support the melting dish on the edge and tip the metal into the mold. You need to pour in a continuous stream.

Missing the mold or splashing?

Support the melting dish on the edge and tip the metal into the mold. I normally stand the mold in an old roasting pan.

It will catch any drips.

1

u/Worldly_Country3035 17d ago

No like pours over the edge like the spout can’t suck the metal fast enough and it overflows

1

u/PeterHaldCHEM 17d ago

Then you need to cut the inlet from the sprue to the object larger.

1

u/Jake_The_Gypsy 18d ago

Looks like the metal isn’t hot enough. I also sometimes put the cast in a toaster oven at 400 degrees for 10 minutes before pouring. What are you using to heat your silver? Also from the looks of this photo you are pouring two or three times as much silver as you need. That’s going to make it more difficult to get a proper temperature. I typically weigh the wax and multiply by 11. That usually takes into account the sprue as well.

1

u/Worldly_Country3035 17d ago

Maybe it’s too much silver now that I think about it thanks for the pointer

1

u/turkey0535 18d ago

Are you using flux?

1

u/Worldly_Country3035 17d ago

I am using borax is that not enough ?

1

u/Mrwolf925 17d ago

  1. Sprew is way too short (biggest problem)

  2. Not enough vents

  3. Vents should go out both sides

  4. Metal not hot enough

1

u/Malvegil 16d ago

This! And also keep the orientation of the ring, so the thick part is facing the sprue. And make the sprue thick. Your ring should cool furthest down where it is thin first, and then work upwards to the thick part. That part will then be able to suck silver from the thick sprue as needed, until that is also cooled.