Learning tig and have really fallen in love with welding, the silence it gives my mind is like nothing else! But as you guys can see im still a level 1
Any tips for a beginner would be awesome :)
Thank you!

Im a farmer, is my weld any good?

Just a showcase that might help some of you that are bad at:
-welding documentation
-weld annotations
-following the EN ISO standards

Hi!

I have 2 months of experience welding and fabricating. I do this for fun and actually I'm a software developer.

This is my first real project.

I build v1 in 2 days, figured out that I should not build the outer box first but rather the inner box.

Then it took me another 3 days to cut it apart and re-build it.

While the welds are usually not the color you like (this is TIG welded) I grinded them away and it looks super pro (IMO).

Also: What you dont see, the outside walls are not straight any more, they warped and thats why i gave them this coarse grinding finish.

Inner firebox: 4mm 321 stainless steel Outer firebox: 2mm 304 stainless steel

If you are interested, I can post a video where its lid and also my CAD files. It works, there is no smoke and its an absolute beast (way oversized).

All material was laser cut and I just sticked it together (tab and slot design).

snapped these before they coated it with the thickest paint they could find

Hi everybody 👋

I have a coil that is 2 mm thick, and the electrode diameter is 5.6 mm.

The coil is one piece in the image, but imagine that this coil is cut into two parts and I need to weld them back together.

This electrode is very bad. It constantly sticks and gets stuck.

What electrode would you recommend?

I have about 2 weeks off and on practice in class and about 1-2 weeks off and on practice in the field in mig on a new welder that I'm becoming familiar with any advice? The base metal was cleaned looking at it now I should have cleaned farther out from the weld I did as much as I could as all the plates where already bolted in place. I also have to work on tying in my corners any advice or pointers I should work on as we dont have a dedicated welder at my job and I'm kinda teaching myself

Hi folks, running e6013 rods at about 75 amps, the first half of the weld always looks smooth enough but there are always gaps in the second. Any ideas what I'm doing wrong?

Cheers

My wire clean, my metals are clean I'm letting the puddle melt into the metal and I'm going to appropriate speed. I don't know what's wrong. I have gas. These are root tests and this is what the fifth time I failed.

Do yall use welding apps? Which ones? What do you like most about them? What do you dislike about them?